Temper | Annealed | Cold worked (approx. 20%) | ||||
---|---|---|---|---|---|---|
Material | 316 | 316L | | 316 | 316L | |
Tensile Rm | 75 | 70 | ksi (min) | 102-131 | ksi (min) | |
Tensile Rm | 515 | 485 | MPa (min) | 700-900 | MPa (min) | |
R.p. 0.2% Yield | 30 | 27 | ksi (min) | 73-102 | ksi (min) | |
R.p. 0.2% Yield | 205 | 182 | MPa (min) | 500-700 | MPa (min) | |
Elongation (2” or 4D gl) | 35 | % (min) | 40 | % (min) |
316 | 316L | |||
---|---|---|---|---|
Element | Min | Max | Min | Max |
C | - | 0.08 | - | 0.35 |
Mn | - | 2 | - | 2 |
Ni | 10 | 14 | 10 | 15 |
Cr | 16 | 18 | 16 | 18 |
Mo | 2 | 3 | 2 | 3 |
S | - | 0.03 | - | 0.03 |
Si | - | 1 | - | 1 |
P | - | 0.045 | - | 0.045 |
Temper | Annealed | Cold worked (approx. 20%) | ||||
---|---|---|---|---|---|---|
Material | 316 | 316L | | 316 | 316L | |
Tensile Rm | 75 | 70 | ksi (min) | 102-131 | ksi (min) | |
Tensile Rm | 515 | 485 | MPa (min) | 700-900 | MPa (min) | |
R.p. 0.2% Yield | 30 | 27 | ksi (min) | 73-102 | ksi (min) | |
R.p. 0.2% Yield | 205 | 182 | MPa (min) | 500-700 | MPa (min) | |
Elongation (2” or 4D gl) | 35 | % (min) | 40 | % (min) |
316 | 316L | |||
---|---|---|---|---|
Element | Min | Max | Min | Max |
C | - | 0.08 | - | 0.35 |
Mn | - | 2 | - | 2 |
Ni | 10 | 14 | 10 | 15 |
Cr | 16 | 18 | 16 | 18 |
Mo | 2 | 3 | 2 | 3 |
S | - | 0.03 | - | 0.03 |
Si | - | 1 | - | 1 |
P | - | 0.045 | - | 0.045 |