% | Fe | Cr | Ni | Mo | C | Mn | Si | P | S | Cu | N |
---|---|---|---|---|---|---|---|---|---|---|---|
min | balance | 19.5 | 17.5 | 6.0 | | | | | | 0.50 | 0.18 |
max | 20.5 | 18.5 | 6.5 | 0.020 | 1.00 | 0.80 | 0.030 | 0.010 | 1.00 | 0.22 |
Density | 7.94 g/cm3 |
Melting range | 1320-1390℃ |