Alloy | % | Ni | Mo | Fe | Cr | Co | C | Mn | V | Si | P | S |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Hastelloy B | Min. | Balance | 26 | 4.0 | | | | | 0.2 | | | |
Max. | 30 | 6.0 | 1.0 | 2.5 | 0.05 | 1.0 | 0.4 | 1.0 | 0.04 | 0.03 | ||
Hastelloy B-2 | Min. | Balance | 26 | 2.0 | | | | | | | | |
Max. | 30 | 7.0 | 1.0 | 1.0 | 0.02 | 1.0 | | 0.1 | 0.04 | 0.03 |
Density | 9.24g/cm3 |
Melting point | 1330-1380℃ |
Alloy state | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
Hastelloy B | 690 | 310 | 40 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B622 | B619 | B622 | B626 | B333 | B335 | B564 | B366 |
Alloy | % | Ni | Mo | Fe | Cr | Co | C | Mn | V | Si | P | S |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Hastelloy B | Min. | Balance | 26 | 4.0 | | | | | 0.2 | | | |
Max. | 30 | 6.0 | 1.0 | 2.5 | 0.05 | 1.0 | 0.4 | 1.0 | 0.04 | 0.03 | ||
Hastelloy B-2 | Min. | Balance | 26 | 2.0 | | | | | | | | |
Max. | 30 | 7.0 | 1.0 | 1.0 | 0.02 | 1.0 | | 0.1 | 0.04 | 0.03 |
Density | 9.24g/cm3 |
Melting point | 1330-1380℃ |
Alloy state | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
Hastelloy B | 690 | 310 | 40 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B622 | B619 | B622 | B626 | B333 | B335 | B564 | B366 |