% | Ni | Cr | Mo | Fe | Co | C | Mn | Si | P | S | Cu | Al |
---|---|---|---|---|---|---|---|---|---|---|---|---|
min | balance | 22.0 | 15.0 | | | | | | | | 1.3 | |
max | 24.0 | 17.0 | 3.0 | 2.0 | 0.010 | 0.50 | 0.08 | 0.025 | 0.010 | 1.9 | 0.50 |
Density | 8.50 g/cm3 |
Melting range | 1328-1358℃ |
% | Ni | Cr | Mo | Fe | Co | C | Mn | Si | P | S | Cu | Al |
---|---|---|---|---|---|---|---|---|---|---|---|---|
min | balance | 22.0 | 15.0 | | | | | | | | 1.3 | |
max | 24.0 | 17.0 | 3.0 | 2.0 | 0.010 | 0.50 | 0.08 | 0.025 | 0.010 | 1.9 | 0.50 |
Density | 8.50 g/cm3 |
Melting range | 1328-1358℃ |