Alloy | % | Ni | Cr | Mo | Fe | W | Co | C | Mn | Si | V | P | S |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Min. | balance | 14.5 | 15 | 4 | 3 | | | | | | | |
Max. | 16.5 | 17 | 7 | 4.5 | 2.5 | 0.08 | 1 | 1 | 0.35 | 0.04 | 0.03 | ||
C22 | Min. | balance | 20.0 | 12.5 | 2 | 2.5 | | | | | | | |
Max. | 22.5 | 14.5 | 6 | 3.5 | 2.5 | 0.015 | 0.5 | 0.08 | 0.35 | 0.02 | 0.02 |
Density | 8.9 g/cm³ |
Melting point | 1325-1370 ℃ |
Alloy state | Tensile strength Rm N/mm² | Yield strength R P 0.2 N/mm² | Elongation A 5 % |
Hastelloy C22 | 690 | 283 | 40 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B622 | B619 | B622 | B626 | B575 | B574 | B564 | B366 |
Alloy | % | Ni | Cr | Mo | Fe | W | Co | C | Mn | Si | V | P | S |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Min. | balance | 14.5 | 15 | 4 | 3 | | | | | | | |
Max. | 16.5 | 17 | 7 | 4.5 | 2.5 | 0.08 | 1 | 1 | 0.35 | 0.04 | 0.03 | ||
C22 | Min. | balance | 20.0 | 12.5 | 2 | 2.5 | | | | | | | |
Max. | 22.5 | 14.5 | 6 | 3.5 | 2.5 | 0.015 | 0.5 | 0.08 | 0.35 | 0.02 | 0.02 |
Density | 8.9 g/cm³ |
Melting point | 1325-1370 ℃ |
Alloy state | Tensile strength Rm N/mm² | Yield strength R P 0.2 N/mm² | Elongation A 5 % |
Hastelloy C22 | 690 | 283 | 40 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B622 | B619 | B622 | B626 | B575 | B574 | B564 | B366 |