Alloy | % | Ni | Cr | Mo | Fe | C | Mn | Si | Co | S | P | Ti |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C-4 | Min. | 65 | 14 | 14 | | | | | | | | |
Max. | | 18 | 17 | 3.0 | 0.01 | 1.0 | 0.08 | 2.0 | 0.010 | 0.025 | 0.70 |
Density | 8.64 g/cm3 |
Melting point | 1350-1400 ℃ |
Alloy | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
C-4 | 783 | 365 | 55 |
Alloy | % | Ni | Cr | Mo | Fe | C | Mn | Si | Co | S | P | Ti |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C-4 | Min. | 65 | 14 | 14 | | | | | | | | |
Max. | | 18 | 17 | 3.0 | 0.01 | 1.0 | 0.08 | 2.0 | 0.010 | 0.025 | 0.70 |
Density | 8.64 g/cm3 |
Melting point | 1350-1400 ℃ |
Alloy | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
C-4 | 783 | 365 | 55 |