Alloy | % | Ni | Cr | Fe | C | Mn | Si | Cu | P | S |
---|---|---|---|---|---|---|---|---|---|---|
600 | Min. | 72 | 14 | 6 | | | | | | |
Max. | | 17 | 10 | 0.15 | 1 | 0.5 | 0.5 | 0.015 | 0.015 |
Density | 8.4 g/cm³ |
Melting Point | 1370-1425 ℃ |
Aolly status | Tensile strength Rm N/mm² | Yield strength R P 0. 2N/mm² | Elongation A 5 % | Brinell hardness HB |
---|---|---|---|---|
Annealing treatment | 550 | 240 | 30 | ≤195 |
Solution treatment | 500 | 180 | 35 | ≤185 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B167 | B517 | B163 | B516 | B168 | B166 | B564 | B366 |
Alloy | % | Ni | Cr | Fe | C | Mn | Si | Cu | P | S |
---|---|---|---|---|---|---|---|---|---|---|
600 | Min. | 72 | 14 | 6 | | | | | | |
Max. | | 17 | 10 | 0.15 | 1 | 0.5 | 0.5 | 0.015 | 0.015 |
Density | 8.4 g/cm³ |
Melting Point | 1370-1425 ℃ |
Aolly status | Tensile strength Rm N/mm² | Yield strength R P 0. 2N/mm² | Elongation A 5 % | Brinell hardness HB |
---|---|---|---|---|
Annealing treatment | 550 | 240 | 30 | ≤195 |
Solution treatment | 500 | 180 | 35 | ≤185 |
Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting |
---|---|---|---|---|---|---|---|
B167 | B517 | B163 | B516 | B168 | B166 | B564 | B366 |