Grade | Ni% | Cr% | Fe% | C% | Mn% | Si% | N% | Mo% | Nb% | V% | P% | S% |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Nitronic 50 | 11.5-13.5 | 20.5-23.5 | 52-62 | Max 0.06 | 4.0-6.0 | Max 1.0 | 0.2-0.4 | 1.5-3.0 | 0.1-0.3 | 0.1-0.3 | Max 0.04 | Max 0.03 |
Grade | Density | Melting Point |
---|---|---|
Nitronic 50 | 7.8 g/cm3 | 1415 °C-1450 °C |
Condition | Tensile Strength | Yield Strength σp0.2/MPa | Elongation | Reduction% |
Solution Treated | Min 690 Mpa | Min 380 Mpa | Min 35% | Min 55% |
Grade | Ni% | Cr% | Fe% | C% | Mn% | Si% | N% | Mo% | Nb% | V% | P% | S% |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Nitronic 50 | 11.5-13.5 | 20.5-23.5 | 52-62 | Max 0.06 | 4.0-6.0 | Max 1.0 | 0.2-0.4 | 1.5-3.0 | 0.1-0.3 | 0.1-0.3 | Max 0.04 | Max 0.03 |
Grade | Density | Melting Point |
---|---|---|
Nitronic 50 | 7.8 g/cm3 | 1415 °C-1450 °C |
Condition | Tensile Strength | Yield Strength σp0.2/MPa | Elongation | Reduction% |
Solution Treated | Min 690 Mpa | Min 380 Mpa | Min 35% | Min 55% |