| Grade | C% | Mn% | S% | P% | Si% | Cr% | Ni% | N% |
|---|---|---|---|---|---|---|---|---|
| Nitronic 60 | Max 0.10 | 7.0-9.0 | Max 0.03 | Max 0.04 | 3.5-4.5 | 16.0-18.0 | 8.0-9.0 | 0.08-0.18 |
| Grade | Density | Melting Point |
|---|---|---|
| Nitronic 60 | 8.0 g/cm3 | 1375 °C |
| Condition | Tensile Strength | Yield Strength σp0.2/MPa | Elongation | Reduction% | Brinell Hardness |
|---|---|---|---|---|---|
| Solution Treated | Min 655 Mpa | Min 345 Mpa | Min 35% | Min 55% | Max 241 |